ZIRCONIA TECH DATA
|
ITEM |
UNIT |
Zro2 |
ZTA |
|
Density |
G/cm3 |
6.05 |
413 |
|
Bending Resistance |
Mpa |
1300 |
1000 |
|
Compressive Strength |
Mpa |
3000 |
3300 |
|
Elasticity Modulus |
Gpa |
205 |
320 |
|
Shock Strength |
Mpam/2 |
12 |
10 |
|
Vaporization Coefficient |
M |
25 |
20 |
|
Vickers Hardness |
HV0.5 |
1200 |
1700 |
|
Thermal Expansivity |
10-6K-1 |
10 |
9 |
|
Conductivity |
W/MK |
2 |
20 |
|
Thermal Shock Resistance |
AT℃ |
280 |
260 |
|
Maximum Service Temperature |
℃ |
1200 |
1600 |
|
20℃ Volume Resistance |
Ω |
≥1010 |
≥1012 |
|
Dielectric Strength |
KV/mm |
- |
- |
|
Apparent Porosity |
％ |
0 |
0 |
|
Permittivity |
Er |
- |
- |
|
Dielectric Loss Angle |
tanδ |
- |
- |
ZIRCONIA POWDER TECH DATA
|
Check Items |
Results |
|
Composition |
ZrO2(HFO2)/Y2O3=94.48/5.22wt％ |
|
Al2O3 Conten |
0.25％ |
|
SiO2 Conten |
18.12ppm |
|
Fe2O3 Conten |
31.16ppm |
|
Na2O Conten |
8.1ppm |
|
Cl-Conten |
48.37ppm |
|
Surface Area |
7.38m2/g |
|
Original Particle Size |
32nm |
|
Size Distribution |
224nm |
|
Igition Loss |
3.17％(1100℃) |
|
Apparent Density |
1.24g/cm3 |
הצהרת פרטיות: הפרטיות שלך חשובה לנו מאוד. החברה שלנו מבטיחה לא לחשוף את המידע האישי שלך לכל אקסני עם ההרשאות המפורשות שלך.
מלא מידע נוסף כך שיוכל ליצור איתך קשר מהר יותר
הצהרת פרטיות: הפרטיות שלך חשובה לנו מאוד. החברה שלנו מבטיחה לא לחשוף את המידע האישי שלך לכל אקסני עם ההרשאות המפורשות שלך.
צור קשר עכשיו