נתונים טכניים של אלומינה
|
ITEM |
UNIT |
99.9 ALUMINA |
|
Density |
G/cm3 |
3.94 |
|
Bending Resistance |
Mpa |
500 |
|
Compressive Strength |
Mpa |
3300 |
|
Elasticity Modulus |
Gpa |
400 |
|
Shock Strength |
Mpam/2 |
5.2 |
|
Vaporization Coefficient |
M |
12 |
|
Vickers Hardness |
HV0.5 |
2000 |
|
Thermal Expansivity |
10-6K-1 |
8.0 |
|
Conductivity |
W/MK |
28 |
|
Thermal Shock Resistance |
AT℃ |
280 |
|
Maximum Service Temperature |
℃ |
1750 |
|
20℃ Volume Resistance |
Ω |
≥1015 |
|
Dielectric Strength |
KV/mm |
30 |
|
Apparent Porosity |
％ |
0 |
|
Permittivity |
Er |
10 |
|
Dielectric Loss Angle |
tanδ |
0.001 |
ALUMINA POWDER TECH DATA
|
ITEM |
LS-110 |
LS-120 |
LS-130 |
LS-110F |
LS-220 |
LS-210 |
|
LOI(％) |
0.02 |
0.02 |
0.05 |
0.08 |
0.03 |
0.01 |
|
Na2O(％) |
0.05 |
0.04 |
0.03 |
0.05 |
0.07 |
0.08 |
|
SiO2(％) |
0.07 |
0.07 |
0.07 |
0.09 |
0.02 |
0.02 |
|
Fe2O3(％) |
0.03 |
0.03 |
0.03 |
0.03 |
0.02 |
0.02 |
|
Al2O3(％) |
99.9 |
99.9 |
99.9 |
99.9 |
99.9 |
99.9 |
|
average grain diameter(um) |
1.7 |
2.1 |
2.2 |
1.1 |
2.7 |
2.9 |
|
αgrain diameter(um) |
1-2 |
1-3 |
2-4 |
1-2 |
2-3 |
3-5 |
|
BET Surface Area(m2/g) |
1.9 |
1.4 |
1.4 |
3.2 |
1.6 |
0.9 |
|
Pressure-induced volume density(g/cm3)* |
2.22 |
2.27 |
2.31 |
2.29 |
2.22 |
2.32 |
|
Forming density(g/cm3)** |
2.13 |
2.20 |
2.23 |
2.33 |
2.17 |
2.30 |
|
Sintering volume density(g/cm3)** |
3.78 |
3.79 |
3.78 |
3.89 |
3.81 |
3.77 |
|
Line collection efficiency(％) |
18.0 |
17.2 |
16.7 |
15.7 |
17.5 |
15.3 |
הצהרת פרטיות: הפרטיות שלך חשובה לנו מאוד. החברה שלנו מבטיחה לא לחשוף את המידע האישי שלך לכל אקסני עם ההרשאות המפורשות שלך.
מלא מידע נוסף כך שיוכל ליצור איתך קשר מהר יותר
הצהרת פרטיות: הפרטיות שלך חשובה לנו מאוד. החברה שלנו מבטיחה לא לחשוף את המידע האישי שלך לכל אקסני עם ההרשאות המפורשות שלך.
צור קשר עכשיו